doppel-lag-602改性硅流平剂
silicone surface additive for solvent-borne coating systems with a medium reduction of surface tension and a medium increase of surface slip.
product data
composition
solution of a polyether-modified polydimethylsiloxane.
typical properties
the values indicated in this data sheet describe typical properties and do not constitute specification limits.
density (20 °c): 0.94 g/ml
non-volatile matter (30 min., 150 °c): 52 %
solvents: xylene/isobutanol
flash point: 25 °c
coatings industry
special features and benefits
the additive provides a medium reduction of surface tension in the coating systems. it increases slip and improves leveling and gloss. silicone additives prevent the formation of bénard cells.also improves substrate wetting and anti-blocking properties
recommended use
lag 602 is broadly compatible and suitable for all solvent-borne systems.
recommended levels
0.1-0.3 % additive (as supplied) based upon total formulation
the above recommended levels can be used for orientation. optimal levels are determined through a series of laboratory tests.
incorporation and processing instructions
the additive can be incorporated during any stage of the production process, including post-addition.
thinning before incorporation may make dosing easier
special note
unlike so-called silicone oils, this additive is very user-friendly. however, before use, one should determine in test series whether foam is stabilized in certain systems and check the recoatability and crater development
溶剂型
体系
流平剂levelling agent
产品型号
product model
固含量wt%
化学组成
composition
特点与优点
special features and benefits
推荐应用
recommended use
lag-613
100%
改性硅氧烷溶液
强烈降低体系的动态和静态表面张力
不稳泡、不影响重涂并且对表面滑爽没有影响
提高在特别难以润湿的基材表面的润湿
水性涂料
无溶剂 uv 涂料
lag-614
100%
含羟基官能团的有机硅改性聚丙烯酸酯溶液
提高溶剂型涂料易清洁性能的有机硅表面助剂。含有羟基官能团，交联后具有永久的易清洁效果
溶剂型面漆
lag-615
50%
水性丙烯酸酯
降低体系的表面张力，促进流平，增进底材润湿性，增进表面滑爽性和光泽。
是性能良好的通用型的流平剂。
通用于水性体系
lag-616
70%
氟碳改性丙烯酸酯
促进流平
提高底材润湿
不影响层间附着力
可二次重涂
附增消泡和脱泡效果
类似efka-3772丙烯酸聚氨酯、
醇酸聚氨酯、聚酯树脂、
热塑性丙烯酸树脂、
环氧树脂、氨基体系
lag-617
类似efka-3777