说明：113-48是一种极为灵活、电绝缘的油墨、涂料和粘合剂。
通过冲压、丝网印刷、浸渍和注射器分配应用。本产品具有良好的附着力
到卡普顿，聚酯薄膜，玻璃，和其他各种表面。与传统绝缘材料不同，这种产品
非常抗弯曲和折皱。113-48的一些应用包括但不限于绝缘
聚酰亚胺柔性电路、聚合物厚膜电路和薄膜开关。113-48是
104-38岁。
典型固化特性：
稠稠液体
抗皱性佳
体积电阻率（ω-cm）1 x 1011
介电强度（伏特/密耳）525
硬度（肖氏硬度d）55
抗拉强度（psi）6500
抗撕裂性（磅/英寸）>300
水汽透过率低
建议的处理和固化：113-48已准备好供应使用。进一步变薄可能是
通过添加少量cmi稀释剂102-03和/或醋酸丁酯来完成。性能
大多数应用是在使用200-300瓦/英寸汞蒸气灯进行固化后，再进行
在150°c到180°c下几分钟。典型的固化时间从几秒到一分钟不等，具体取决于
可用能量。通过使用200-300固化剂在多种基材上获得良好的性能
瓦特/英寸汞蒸气灯，随后在50°c至180°c的温度范围内进行后固化。最终用户
建议通过实验确定最适合个人应用的温度和时间。
储存：保存在密封的不透明容器中，在25℃下保存6个月。
安全和操作：在通风良好的情况下使用。远离火花和明火。避免长时间
接触皮肤和吸入蒸汽。用肥皂和水清洗皮肤。
113-48dielectric ink绝缘油墨
description: 113-48 is an extremely flexible, electrically insulating ink, coating and adhesive suitable for
application by stamping, screen printing, dipping and syringe dispensing. this product features excellent adhesion
to kapton, mylar, glass, and a variety of other surfaces. unlike conventional insulating materials, this product is
very resistant to flexing and creasing. some applications for 113-48 include, but are not limited to, insulating
polyimide flexible circuits, polymer thick film circuitry, and membrane switches. 113-48 is a crosslinking version of
104-38.
typical cured properties:
consistency thick liquid
crease resistance excellent
volume resistivity (ω-cm) 1 x 1011
dielectric strength (volts/ mil) 525
hardness (shore d) 55
tensile strength (psi) 6500
tear resistance (lbs/in) > 300
moisture vapor transmission low
suggested handling & curing: 113-48 is ready to use as supplied. further thinning may be
accomplished by adding small amounts of cmi thinner # 102-03 and/or butyl cellosolve acetate. best properties for
most applications result when cured using a 200-300 watt/inch mercury vapor lamp, followed by a post cure for
several minutes at 150°c to 180°c.typical cure time varies from a few seconds to a minute, depending on the
amount of energy available. good properties are obtained on a variety of substrates by curing using a 200-300
watt/inch mercury vapor lamp, followed by a post cure for at temperatures ranging from 50°c to 180°c. end user is
advised to experimentally determine temperature and time best suited for individual applications.
storage: shelf life: 6 months at 25°c, when kept in a sealed opaque container.
safety & handling: use with adequate ventilation. keep away from sparks and open flames. avoid prolonged
contact with skin and breathing of vapors. wash with soap and water to remove from skin.