tpe美国杜邦 5556
物理性能额定值 (公制)额定值 (英制)测试方法密度1.03 g/cc0.0372 lb/in³
1.19 g/cc0.0430 lb/in³iso 1183吸水率0.60 %@thickness 2.00 mm
0.60 %@thickness 0.0787 in
sim. to iso 62水分吸收0.200 %@thickness 2.00 mm
0.200 %@thickness 0.0787 in
sim. to iso 62饱和吸水率0.60 %0.60 %immersion 24h; astm d570粘度81295 cp@shear rate 5000 1/s, temperature 240 °c
81295 cp@shear rate 5000 1/s, temperature 464 °f
iso 11403-1 -2
88320 cp@shear rate 5000 1/s, temperature 230 °c
88320 cp@shear rate 5000 1/s, temperature 446 °f
iso 11403-1 -2
96440 cp@shear rate 5000 1/s, temperature 220 °c
96440 cp@shear rate 5000 1/s, temperature 428 °f
iso 11403-1 -2
321800 cp@shear rate 500 1/s, temperature 240 °c
321800 cp@shear rate 500 1/s, temperature 464 °f
iso 11403-1 -2
358400 cp@shear rate 500 1/s, temperature 230 °c
358400 cp@shear rate 500 1/s, temperature 446 °f
iso 11403-1 -2
400200 cp@shear rate 500 1/s, temperature 220 °c
400200 cp@shear rate 500 1/s, temperature 428 °f
iso 11403-1 -2线性成型收缩率,flow0.014 cm/cm0.014 in/iniso 294-4 2577线性成型收缩率，横向0.014 cm/cm0.014 in/iniso 294-4 2577熔体流动速率7.0 g/10 min@load 2.16 kg, temperature 220 °c
7.0 g/10 min@load 4.76 lb, temperature 428 °f
cm³/10min; iso 1133
7.8 g/10 min@load 2.16 kg, temperature 220 °c
7.8 g/10 min@load 4.76 lb, temperature 428 °f
iso 1133机械性能额定值 (公制)额定值 (英制)测试方法肖氏硬度 (邵氏 d)515115s; iso 868
<= 55<= 55iso 868抗张强度(断裂)40.0 mpa5800 psiiso 527-1/-2抗张强度6.90 mpa@strain 5.00 %
1000 psi@strain 5.00 %
iso 527-1/-2
11.0 mpa@strain 10.0 %
1600 psi@strain 10.0 %
iso 527-1/-2
14.5 mpa@strain 50.0 %
2100 psi@strain 50.0 %
iso 527-1/-2
16.0 mpa@strain 100 %
2320 psi@strain 100 %
iso 527-1/-2
3.97 mpa@strain 6.94 %, temperature 120 °c
576 psi@strain 6.94 %, temperature 248 °f
tpe; iso 11403-1 -2
4.65 mpa@strain 6.90 %, temperature 100 °c
674 psi@strain 6.90 %, temperature 212 °f
tpe; iso 11403-1 -2
4.93 mpa@strain 6.00 %, temperature 90.0 °c
715 psi@strain 6.00 %, temperature 194 °f
iso 11403-1 -2
4.97 mpa@strain 6.87 %, temperature 90.0 °c
721 psi@strain 6.87 %, temperature 194 °f
tpe; iso 11403-1 -2
5.78 mpa@strain 16.44 %, temperature 120 °c
838 psi@strain 16.44 %, temperature 248 °f
tpe; iso 11403-1 -2
6.37 mpa@strain 26.67 %, temperature 120 °c
924 psi@strain 26.67 %, temperature 248 °f
tpe; iso 11403-1 -2
6.55 mpa@strain 36.16 %, temperature 120 °c
950 psi@strain 36.16 %, temperature 248 °f
tpe; iso 11403-1 -2
6.62 mpa@strain 46.39 %, temperature 120 °c
960 psi@strain 46.39 %, temperature 248 °f
tpe; iso 11403-1 -2
6.70 mpa@strain 58.81 %, temperature 120 °c
972 psi@strain 58.81 %, temperature 248 °f
tpe; iso 11403-1 -2
6.83 mpa@strain 71.96 %, temperature 120 °c
991 psi@strain 71.96 %, temperature 248 °f
tpe; iso 11403-1 -2
6.84 mpa@strain 7.55 %, temperature 60.0 °c
992 psi@strain 7.55 %, temperature 140 °f
tpe; iso 11403-1 -2
6.97 mpa@strain 85.11 %, temperature 120 °c
1010 psi@strain 85.11 %, temperature 248 °f
tpe; iso 11403-1 -2
6.98 mpa@strain 17.06 %, temperature 100 °c
1010 psi@strain 17.06 %, temperature 212 °f
tpe; iso 11403-1 -2
7.12 mpa@strain 98.26 %, temperature 120 °c
1030 psi@strain 98.26 %, temperature 248 °f
tpe; iso 11403-1 -2
7.41 mpa@strain 117.99 %, temperature 120 °c
1070 psi@strain 117.99 %, temperature 248 °f
tpe; iso 11403-1 -2
7.46 mpa@strain 6.00 %, temperature 40.0 °c
1080 psi@strain 6.00 %, temperature 104 °f
iso 11403-1 -2
7.51 mpa@strain 16.99 %, temperature 90.0 °c
1090 psi@strain 16.99 %, temperature 194 °f
tpe; iso 11403-1 -2
7.67 mpa@strain 27.23 %, temperature 100 °c
1110 psi@strain 27.23 %, temperature 212 °f
tpe; iso 11403-1 -2
7.67 mpa@strain 131.14 %, temperature 120 °c
1110 psi@strain 131.14 %, temperature 248 °f
tpe; iso 11403-1 -2
7.88 mpa@strain 37.39 %, temperature 100 °c
1140 psi@strain 37.39 %, temperature 212 °f
tpe; iso 11403-1 -2
7.90 mpa@strain 6.00 %, temperature 23.0 °c
1150 psi@strain 6.00 %, temperature 73.4 °f
iso 11403-1 -2
7.96 mpa@strain 46.83 %, temperature 100 °c
1150 psi@strain 46.83 %, temperature 212 °f
tpe; iso 11403-1 -2
8.04 mpa@strain 60.62 %, temperature 100 °c
1170 psi@strain 60.62 %, temperature 212 °f
tpe; iso 11403-1 -2
8.07 mpa@strain 147.21 %, temperature 120 °c
1170 psi@strain 147.21 %, temperature 248 °f
tpe; iso 11403-1 -2
8.17 mpa@strain 73.69 %, temperature 100 °c
1180 psi@strain 73.69 %, temperature 212 °f
tpe; iso 11403-1 -2
8.30 mpa@strain 27.11 %, temperature 90.0 °c
1200 psi@strain 27.11 %, temperature 194 °f
tpe; iso 11403-1 -2
8.32 mpa@strain 86.76 %, temperature 100 °c
1210 psi@strain 86.76 %, temperature 212 °f
tpe; iso 11403-1 -2
8.52 mpa@strain 100.56 %, temperature 100 °c
1240 psi@strain 100.56 %, temperature 212 °f
tpe; iso 11403-1 -2
8.52 mpa@strain 24.0 %, temperature 90.0 °c
1240 psi@strain 24.0 %, temperature 194 °f
iso 11403-1 -2
8.56 mpa@strain 37.24 %, temperature 90.0 °c
1240 psi@strain 37.24 %, temperature 194 °f
tpe; iso 11403-1 -2
8.65 mpa@strain 47.36 %, temperature 90.0 °c
1250 psi@strain 47.36 %, temperature 194 °f
tpe; iso 11403-1 -2
8.67 mpa@strain 7.52 %, temperature 40.0 °c
1260 psi@strain 7.52 %, temperature 104 °f
tpe; iso 11403-1 -2
8.76 mpa@strain 170.59 %, temperature 120 °c
1270 psi@strain 170.59 %, temperature 248 °f
tpe; iso 11403-1 -2
8.78 mpa@strain 60.37 %, temperature 90.0 °c
1270 psi@strain 60.37 %, temperature 194 °f
tpe; iso 11403-1 -2
8.85 mpa@strain 120.16 %, temperature 100 °c
1280 psi@strain 120.16 %, temperature 212 °f
tpe; iso 11403-1 -2
8.94 mpa@strain 73.39 %, temperature 90.0 °c
1300 psi@strain 73.39 %, temperature 194 °f
tpe; iso 11403-1 -2
9.14 mpa@strain 87.12 %, temperature 90.0 °c
1330 psi@strain 87.12 %, temperature 194 °f
tpe; iso 11403-1 -2
9.17 mpa@strain 133.96 %, temperature 100 °c
1330 psi@strain 133.96 %, temperature 212 °f
tpe; iso 11403-1 -2
9.33 mpa@strain 100.14 %, temperature 90.0 °c
1350 psi@strain 100.14 %, temperature 194 °f
tpe; iso 11403-1 -2
9.60 mpa@strain 196.16 %, temperature 120 °c
1390 psi@strain 196.16 %, temperature 248 °f
tpe; iso 11403-1 -2
9.61 mpa@strain 150.65 %, temperature 100 °c
1390 psi@strain 150.65 %, temperature 212 °f
tpe; iso 11403-1 -2
9.71 mpa@strain 120.38 %, temperature 90.0 °c
1410 psi@strain 120.38 %, temperature 194 °f
tpe; iso 11403-1 -2
9.82 mpa@strain 17.63 %, temperature 60.0 °c
1420 psi@strain 17.63 %, temperature 140 °f
tpe; iso 11403-1 -2
10.01 mpa@strain 133.4 %, temperature 90.0 °c
1452 psi@strain 133.4 %, temperature 194 °f
tpe; iso 11403-1 -2tpe是热塑性聚氨酯弹性体橡胶。主要分为硬度范围宽（0-85d）、耐磨、耐油，透明，弹性好，在日用品、体育用品、玩具、装饰材料等领域得到广泛应用，无卤阻燃tpe还可以代替软质pvc以满足越来越多领域的环保要求，tpe出现在2015年，tpe薄膜消费量约占tpe产品总消费量的20%，tpe薄膜平均销售价格约4万元/吨，按照2013年我国tpe产品消费量23万吨计算，tpe薄膜消费量约为4.6万吨，市场消费额约18.4亿元，预计，2013-2017年 tpe市场规模年均增长速度为11.2%，2017年达到28.1亿元，tpe现在是越来越受到大家欢迎。