硅胶键盘具有环保，无毒无味，并且弹性好；耐磨损，耐高温，不变形等特点，可以长期使用；外表光滑，手感强，是真正的绿色环保用品。
siliconekeyboard with environmentalprotection,non-toxic andtasteless,and goodelasticity; wearresistance, high temperatureresistance, nodeformation, can be used for a long time; the appearance ofsmooth, strong handfeeling,is the real greenproducts.
1，客户提出需求，一般这种需求都是体现的标准图纸或者样品上。 customerdemand, thisdemand isgenerally reflectthe standard drawings orsamples,.
2，模具厂开模具，模具厂有很多种，最好找专业开按键模具的厂做，专业的细节他们比较好把握。open moldmoldfactory, moldfactory has manykinds, it is best tofind aprofessional to open thekey mold factory, professional detailsthey bettergrasp.
3，原料准备 主要是炼胶，炼胶要把握颜色，硬度，弹力等因素。raw materialpreparation ismainly rubber,rubber to graspthecolor,hardness, elasticetc..
4，试模具，也叫打样。实际操作过程中，很多客户都需要先打样品，这样的话，开模具的时候就只需要开
   样品模具，打样开样品模具，为了是节省成本。trytodie,also calledproofing. in theactual operationprocess, manycustomers arerequired to make thesample,if so,when openmold needonly toopen
5，上机做大货，基本上样品无差别后，就要上机做大货，如果打样和预期效果不一样，需要另外再修改模具
  准备好后合模进行加热、加压硫化。硫化的主要控制参数为温度、压力和硫化时间，其典型操作工艺条件为：温度160℃±10℃；压力15～20mpa；时间150～200s(视键的高度而定，如key型较矮较小30～40s也可完成)。硫化完成后，将模具推出硫化  机，小心掀开母模，用风枪配合，慢慢将硅胶按键从模具取出即可。 samplemold,mold proofing onsamples, in orderto savecosts.
5, the biggoods,basicallyno differenceafter thesample, willbe the biggoods, ifthe proof and the expected effect isnot the same, needto further modifydie6，二次硫化
硫化后的半成品可按客户要求决定是否进行二次硫化，以除去产品中残存的硫化剂分解产物，提高产品的性能。常规二次硫化采用立式烤箱，用180～200℃的温度烘烤2h即可完成。
readyto dieafterheating,pressurizingvulcanization. the main control parameters astemperature, pressure andcuring curingtime,the typical operating conditions were:temperature 160 ± 10℃; pressure 15 ~ 20mpa;time of 150 ~ 200s(as theheight of the key set, such as type key shorter smaller30 ~ 40s can bedone).curing iscompleted, willdie outvulcanizingmachine,carefully opendie,mix with airgun, slowly the silica gelkeystroke can be removed from themold.
7，表面处理，一般硅胶按键都需要做一些表面处理，最简单是是丝印，稍微复杂点的是彩印，  还有就是镭射雕刻，外加喷油。
the twovulcanization
semi-finished products after curingcan decidewhether the twovulcanizationvulcanizedproducts according to customerrequirements,to removeresidual agent decompositionproducts, improveproductperformance. theconventional twovulcanizationusing verticaloven, bakingtemperature 180～ 200℃ 2h can becompleted.
6，拆边，模具压出来的产品基本都有毛边，这样的话需要人工拆边。surfacetreatment,general siliconekeys will need todo some surfacetreatment, the most simpleis slightly morecomplex is thescreen printing,color printing, there isthe laserengraving, plusinjection.
7，质检，质检在每一部都需要，操作员的自我检查，qc检查等，
remove theedge,die outproducts arerough, so theneed ofartificial remove edge.
7, qualityinspection, quality inspectionin everyneed, theoperator selfinspection,qcinspection,
8，检查无异样后，就可以打包了。check no strange, can be packaged.
1、配料环节
   通常都是半透明的，没有加任何的添加剂和架桥机。如果直接进行加工使用，首先无法硫化成型，然后颜色可能与硅胶产品按键要求不符，再次硬度也达不到产业的需要，这样一来还需要原料进行加工才能够确保配料能够正常使用。
而配料则是根据产品颜色硬度及需要按一定的比例配好。详情见（硅胶的用途）。
　　2、混炼环节
   在上一道工序完成后其次是将配备好的硅胶原料，架桥机，色母及所需的添加剂放入开炼机均匀搅拌。此工序有一定的危险性，如操作不当或不按标准操作的话，很可能对身体有一定伤寒，并且直接影响到硅胶按键的外观及成型品质。