化学气相沉积硒化锌
cvd zinc selenide
硒化锌材料是一种黄色透明的多晶材料，结晶颗粒大小约为70μm，透光范围0.5-15μm。由化学气相沉积
(cvd)方法合成的硒化锌材料基本不存在杂质吸收，散射损失极低。由于对10.6μm 波长光的吸收很小，
对热冲击具有很高的承受能力，使它成为高功率co2 激光器系统中的最佳光学材料。此外在其整个透光波
范围内，也广泛用于不同光学系统中。
zinc selenide is a clear yellow polycrystallinematerial with a grain size of approximately 70
µm,transmitting in the range0.5-15µm.it is essentially free of extrinsic impurity absorptions,
providing extremely low bulk losses from scatter.zincselenide, produced by the method of 
chemical vapour deposition, is the preferred material foroptics used in high power co2 laser 
systems due to its low absorptionand  high resistance to thermal shock making at 10.6µm. 
however it is also a popular choice in systems operating at various bands within 
its widetransmission range.
光学性能 透光波长范围 0.5-15μm 机械性能 杨氏模量 67.2 gpa 
transmission range  young's modulus (9.75 x 106 psi)
体吸收系数  　 断裂模数 55.1 mpa 
bulk absorption   cm-1 mechanical properties rupture modulus (8,000 psi)
coefficient  @ 10.6µm 努氏硬度 105-120 kg/mm2
optical properties 折射率温度系数  　 knoop hardness
temp. change of  61 x 10-6/°c 波森比 0.28
refractive index  @ 10.6µm poisson's ratio
折射率的不均匀性  　 物理性能 化学纯度 99.9996%
refractive index  chemical purity
non-homogeneity @ 632.8 nm 晶体尺寸 50 - 70 μm
热学性能 导热率  0.18 w/cm/°c grain size
thermal conductivity @ 20° c 密度 5.27 g/cm3
比热 0.356 j/g/°c physicalproperties density
thermal properties specific heat 电阻率(ωcm） ≈1012
线性膨胀系数  　 resistivity
linear expansion  7.57 x 10-6/°c 晶体结构crystal 立方
coefficient @ 20° c  structure cubic
硒化锌折射率（n）（20°c室温条件）
indices of refraction (n) of cvd zinc selenide
as a function ofwavelength at room temperature (20°c)
光学折射率 wavelength 折射率 wavelength 折射率 wavelength 折射率 wavelength 折射率 　
(μm) n (μm) n (μm) n (μm) n 　
0.54 2.6754 1.80 2.4496 7.40 2.4201 13.00 2.3850 　
0.58 2.6312 2.20 2.4437 7.80 2.4183 13.40 2.3816 　
0.62 2.5994 2.60 2.4401 8.20 2.4163 13.80 2.3781 　
0.66 2.5755 3.00 2.4376 8.60 2.4143 14.20 2.3744 　
0.70 2.5568 3.40 2.4356 9.00 2.4122 14.60 2.3705 　
0.74 2.5418 3.80 2.4339 9.40 2.4100 15.00 2.3665 　
indices of refraction (n) 0.78 2.5295 4.20 2.4324 9.80 2.4077 15.40 2.3623 　
0.82 2.5193 4.60 2.4309 10.20 2.4053 15.80 2.3579 　
0.86 2.5107 5.0 2.4295 10.60 2.4028 16.20 2.3534 　
0.90 2.5034 5.40 2.4281 11.00 2.4001 16.60 2.3487 　
0.94 2.4971 5.80 2.4266 11.40 2.3974 17.00 2.3438 　
0.98 2.4916 6.20 2.4251 11.80 2.3945 17.80 2.3333 　
1.00 2.4892 6.60 2.4235 12.20 2.3915 18.20 2.3278 　
1.40 2.4609 7.00 2.4218 12.60 2.3883

---