厂家(产地)美国杜邦	牌号FR543
销售方式品牌经销	类型标准料
加工级别注塑级	特性级别阻燃级、 增韧级
用途级别通用级	品牌美国杜邦

比重 1.79 g/cc 1.79 g/cc astm d792
密度 1.79 g/cc 0.0647 lb/in? iso 1183
填料含量 43 % 43 %
water absorption 0.060 %@temperature 23.0 °c
0.060 %@temperature 73.4 °f
50%rh,23°c,24h; astm d570
0.11 %@temperature 23.0 °c
0.11 %@temperature 73.4 °f
equilibrium 50%rh; iso 62, similar to
0.62 %@temperature 23.0 °c
0.62 %@temperature 73.4 °f
saturation, immersed; iso 62, similar to
线性成型收缩率 0.0013 cm/cm@thickness 1.57 mm
0.0013 in/in@thickness 0.0618 in
flow
0.0020 cm/cm@thickness 3.20 mm
0.0020 in/in@thickness 0.126 in
flow
0.0048 cm/cm@thickness 1.57 mm
0.0048 in/in@thickness 0.0618 in
transverse
0.0065 cm/cm@thickness 3.20 mm
0.0065 in/in@thickness 0.126 in
transverse
线性成型收缩率,flow 0.0025 cm/cm 0.0025 in/in annealed; iso 294-4
0.0020 cm/cm@thickness 2.00 mm
0.0020 in/in@thickness 0.0787 in
iso 294-4
线性成型收缩率，横向 0.0105 cm/cm 0.0105 in/in annealed; iso 294-4
0.0075 cm/cm@thickness 2.00 mm
0.0075 in/in@thickness 0.0787 in
iso 294-4
化合物熔体指数 6.0 g/10 min@load 2.16 kg, temperature 280 °c
6.0 g/10 min@load 4.76 lb, temperature 536 °f
cm3/10 min; iso 1133
机械性能额定值 (公制)额定值 (英制)测试方法
洛氏硬度（m 级） 95 95 astm d785
102 102 iso 2039/2
洛氏硬度（r 级） 120 120 astm d785
122 122 iso 2039/2
抗张强度(断裂) 170 mpa@temperature 23.0 °c
24700 psi@temperature 73.4 °f
iso 527
抗张强度 55.2 mpa@temperature 150 °c
8010 psi@temperature 302 °f
astm d638
86.5 mpa@temperature 90.0 °c
12500 psi@temperature 194 °f
astm d638
172 mpa@temperature 23.0 °c
24900 psi@temperature 73.4 °f
astm d638
210 mpa@temperature -40.0 °c
30500 psi@temperature -40.0 °f
astm d638
22.4 mpa@strain 0.470 %, temperature 150 °c
3250 psi@strain 0.470 %, temperature 302 °f
iso 527
27.22 mpa@strain 0.430 %, temperature 120 °c
3948 psi@strain 0.430 %, temperature 248 °f
iso 527
27.5 mpa@strain 0.160 %, temperature 0.000 °c
3990 psi@strain 0.160 %, temperature 32.0 °f
iso 527
28.39 mpa@strain 0.350 %, temperature 90.0 °c
4118 psi@strain 0.350 %, temperature 194 °f
iso 527
29.0 mpa@strain 0.140 %, temperature -40.0 °c
4210 psi@strain 0.140 %, temperature -40.0 °f
iso 527
30.0 mpa@strain 0.210 %, temperature 40.0 °c
4350 psi@strain 0.210 %, temperature 104 °f
iso 527
31.0 mpa@strain 0.180 %, temperature 23.0 °c
4500 psi@strain 0.180 %, temperature 73.4 °f
iso 527
34.9 mpa@strain 0.940 %, temperature 150 °c
5060 psi@strain 0.940 %, temperature 302 °f
iso 527
35.57 mpa@strain 0.310 %, temperature 60.0 °c
5159 psi@strain 0.310 %, temperature 140 °f
iso 527
41.5 mpa@strain 1.41 %, temperature 150 °c
6020 psi@strain 1.41 %, temperature 302 °f
iso 527
41.8 mpa@strain 0.830 %, temperature 120 °c
6060 psi@strain 0.830 %, temperature 248 °f
iso 527
45.7 mpa@strain 1.87 %, temperature 150 °c
6630 psi@strain 1.87 %, temperature 302 °f
iso 527
47.19 mpa@strain 0.690 %, temperature 90.0 °c
6844 psi@strain 0.690 %, temperature 194 °f
iso 527
49.1 mpa@strain 2.34 %, temperature 150 °c
7120 psi@strain 2.34 %, temperature 302 °f
iso 527
50.35 mpa@strain 0.370 %, temperature 40.0 °c
7303 psi@strain 0.370 %, temperature 104 °f
iso 527
50.8 mpa@strain 1.23 %, temperature 120 °c
7370 psi@strain 1.23 %, temperature 248 °f
iso 527
51.7 mpa@strain 2.81 %, temperature 150 °c
7500 psi@strain 2.81 %, temperature 302 °f
iso 527
52.4 mpa@strain 0.320 %, temperature 0.000 °c
7600 psi@strain 0.320 %, temperature 32.0 °f
iso 527
53.8 mpa@strain 3.28 %, temperature 150 °c
7800 psi@strain 3.28 %, temperature 302 °f
iso 527
53.9 mpa@strain 0.280 %, temperature -40.0 °c
7820 psi@strain 0.280 %, temperature -40.0 °f
iso 527
55.0 mpa@strain 0.520 %, temperature 60.0 °c
7980 psi@strain 0.520 %, temperature 140 °f
iso 527
55.6 mpa@strain 3.75 %, temperature 150 °c
8060 psi@strain 3.75 %, temperature 302 °f
iso 527
56.4 mpa@strain 0.350 %, temperature 23.0 °c
8180 psi@strain 0.350 %, temperature 73.4 °f
iso 527
56.85 mpa@strain 1.63 %, temperature 120 °c
8245 psi@strain 1.63 %, temperature 248 °f
iso 527
57.1 mpa@strain 4.21 %, temperature 150 °c
8280 psi@strain 4.21 %, temperature 302 °f
iso 527
58.5 mpa@strain 4.69 %, temperature 150 °c
8480 psi@strain 4.69 %, temperature 302 °f
iso 527
59.61 mpa@strain 1.03 %, temperature 90.0 °c
8646 psi@strain 1.03 %, temperature 194 °f
iso 527
61.26 mpa@strain 2.04 %, temperature 120 °c
8885 psi@strain 2.04 %, temperature 248 °f
iso 527
64.62 mpa@strain 2.44 %, temperature 120 °c
9372 psi@strain 2.44 %, temperature 248 °f
iso 527
67.28 mpa@strain 2.84 %, temperature 120 °c
9758 psi@strain 2.84 %, temperature 248 °f
iso 527
68.2 mpa@strain 1.37 %, temperature 90.0 °c
9890 psi@strain 1.37 %, temperature 194 °f
iso 527
69.36 mpa@strain 3.24 %, temperature 120 °c
10060 psi@strain 3.24 %, temperature 248 °f
iso 527
71.09 mpa@strain 3.65 %, temperature 120 °c
10310 psi@strain 3.65 %, temperature 248 °f
iso 527
71.87 mpa@strain 0.730 %, temperature 60.0 °c
10420 psi@strain 0.730 %, temperature 140 °f
iso 527
72.35 mpa@strain 4.05 %, temperature 120 °c
10490 psi@strain 4.05 %, temperature 248 °f
iso 527
72.8 mpa@strain 0.560 %, temperature 40.0 °c
10600 psi@strain 0.560 %, temperature 104 °f
iso 527
74.5 mpa@strain 0.480 %, temperature 23.0 °c
10800 psi@strain 0.480 %, temperature 73.4 °f
iso 527
74.52 mpa@strain 1.70 %, temperature 90.0 °c
10810 psi@strain 1.70 %, temperature 194 °f
iso 527
75.5 mpa@strain 0.420 %, temperature -40.0 °c
11000 psi@strain 0.420 %, temperature -40.0 °f
iso 527
75.9 mpa@strain 0.470 %, temperature 0.000 °c
11000 psi@strain 0.470 %, temperature 32.0 °f
iso 527
79.34 mpa@strain 2.04 %, temperature 90.0 °c
11510 psi@strain 2.04 %, temperature 194 °f
iso 527
83.14 mpa@strain 2.41 %, temperature 90.0 °c
12060 psi@strain 2.41 %, temperature 194 °f
iso 527
83.19 mpa@strain 0.940 %, temperature 60.0 °c
12070 psi@strain 0.940 %, temperature 140 °f
iso 527
85.76 mpa@strain 2.75 %, temperature 90.0 °c
12440 psi@strain 2.75 %, temperature 194 °f
iso 527

---