| 品牌DOPPEL | 型号LAG-601 |
| 溶解性油性 | 化学成份改性聚硅氧烷 |
| 有效物质含量100（％） ％ | 外观无色至微黄色透明液体 |
| 含量100（％） ％ | 密度1.09–1.13（kg/m3） kg/m3 |
| CAS无 | 包装规格25KG/桶 |
| 规格25KG/桶 |
doppel-lag-601有机硅流平剂
silicone-containing surface additive for ambient-curing plastic systems and solvent-borne coating systems with a strong reduction of surface tension. excellent substrate wetting, prevents cratering and increases surface slip.
product data
composition
solution of a polyether-modified polydimethylsiloxane
typical properties
the values indicated in this data sheet describe typical properties and do not constitute specification limits.
density (20 °c): 0.93 g/ml
non-volatile matter (30 min., 150 °c): 12.5 %
solvents: xylene/monophenyl glycol
flash point: 25 °c
storage and transportation
separation or turbidity may occur at temperatures below 5 °c. warm to 20 °c and mix well.
applications
ambient curing plastic systems
special features and benefits
doppel-lag-601, a highly effective silicone additive, provides a strong reduction of surface tension. it thereby improves the wetting of critical substrates. in pigmented systems it can prevent the formation of bénard cells and improve leveling.
recommended use
doppel-lag-601 is recommended for polyurethane and epoxy systems.
recommended levels
0.1-0.5 % additive (as supplied) based upon total formulation.
the above recommended levels can be used for orientation. optimal levels are determined through a series of laboratory tests.
coatings industry
special features and benefits
the additive provides a strong reduction of the surface tension of the coating systems and is a highly effective silicone additive for wetting critical substrates. doppel-lag-601 improves the acceptance of dust and spray mist and increases surface slip. it reduces air draft sensitivity in wood and furniture coatings and promotes the orientation of matting agents.
recommended levels
0.1-0.5 % additive (as supplied) based upon total formulation
the above recommended levels can be used for orientation. optimal levels are determined through a series of laboratory tests.
溶剂型
体系
流平剂levelling agent
产品型号
product model
固含量wt%
化学组成
composition
特点与优点
special features and benefits
推荐应用
recommended use
lag-601
12.5
聚醚改性甲基硅氧烷
可显著降低表面张力。
改善对难以润湿底材的润湿。
可防止贝纳德漩涡的产生并改善流平性。
所有溶剂型体系
lag-602
52%
聚醚改性聚二甲基硅氧烷
该助剂中等程度降低涂料体系的表面张力
提高滑爽性，增进流平和光泽
提高基材润湿性和抗粘连性能
所有的溶剂型体系
lag-603
100%
聚醚改性聚二甲基硅氧烷
对润湿困难的底材进行良好底材润湿
良好的防缩孔性能
增加了表面滑爽以及耐划伤性和防粘连性
溶剂型体系、
无溶剂体系
水性体系
lag-604
25%
聚酯改性聚二甲基硅氧烷
降低涂料体系的表面张力，改善底材润湿防止缩孔
增加表面滑爽性，提高光泽
所有的溶剂型体系
lag-605
100%
丙烯酸聚酯改性硅氧烷
可反应，高兼容性，
增进滑爽，耐溶剂，耐候，抗黏连
良好的再涂性和覆印性，
平滑性好，流平性好;
推荐用量:0.05~1.0%;
罐头涂料，
透明上光油，
印刷油墨，
塑料涂料，
木器涂料
lag-606
100%
聚醚改性聚二甲基硅氧烷
剧烈降低涂料和印刷油墨的表面张力，改善抗粘连性
提高底材润湿，防止缩孔表面滑爽性和光泽
0.05-0.3 % 助剂用量（供应形式）基于总配方，水性和 uv 体系***多可以添加到 1%
所有溶剂型
无溶剂型
水性涂料
印刷油墨以及罩光油
lag-607
100%
聚醚改性硅氧烷
具有良好的水溶性、平滑性和较低的表面张力
提高抗擦伤性能、重涂性好
改善抗粘连性
可防止针孔且不影响再涂性
溶剂型、无溶剂和水性体系。
适用于涂料、油墨、胶粘剂
室温固化塑料体系
lag-608
45%
聚醚改性硅氧烷
强烈降低水性体系的表面张力
增进流平和基材润湿性
改善抗粘连性
水性涂料
印刷油墨
罩光油
lag-609
100%
聚醚改性的有机硅氧烷
适用于不含有机助溶剂的体系.
降低涂料体系的表面张力，改善底材润湿并防止缩孔
水性涂料水性胶粘剂
印刷油墨 罩光油
lag-610
70?%
聚丙烯酸酯
增进流平和光泽，产生长波效应
丙烯酸酯助剂仅轻微降低表面张力不影响重涂性和层间附着力,该助剂是热稳定的
抗缩孔和流平助剂，可以增进光泽
溶剂型
无溶剂型涂料体系
紫外光固化印刷油墨
罩光清漆
lag-611
52%
聚丙烯酸酯
轻微降低，对重涂性和层间附着力无不利影响
能迅速消除涂膜的缩孔、针孔、鱼眼
对环氧树脂体系有良好的润湿性和平坦性
丙烯酸聚氨酯、醇酸聚氨酯、
聚酯树脂、热塑性丙烯酸树脂、
环氧树脂、氨基体系
lag-612
100
聚丙烯酸酯
增进流平和光泽，产生长波效应
丙烯酸酯助剂仅轻微降低表面张力不影响重涂性和层间附着力,该助剂是热稳定的
抗缩孔和流平助剂，可以增进光泽
不饱和聚酯和环氧树脂
溶剂型
无溶剂型涂料体系